TIG焊接电流对生物医用高氮奥氏体不锈钢接头组织与力学性能的影响
Effects of TIG welding current on the microstructure and mechanical properties of biomedical high-nitrogen austenitic stainless steel joints
摘要
Abstract
To address the compatibility issue between microstructure stability and mechanical property matching during the welding of high-nitrogen austenitic stainless steel,autogenous TIG butt welding was employed.With welding speed and shielding gas conditions kept constant,the welding current was used as the primary variable to systematically investigate its effects on the microstructural zoning characteristics,Cr2N nitride precipitation behavior,and the evolution of mechanical properties of the welded joints.The results reveal that the welded joints exhibit typical microstructural zones,including the weld zone,coarse-grained heat-affected zone,and fine-grained heat-affected zone.Welding current significantly affects the grain characteristics and microstructural uniformity in each zone.XRD analysis indicates that Cr2N is detectable in the weld metal at currents from 160 to 200 A,whereas when the welding current is increased to 220 A and above,the diffraction peaks of Cr2N are significantly weakened and eventually disappear.Based on the analysis of welding thermal cycles,this suggests that higher welding currents kinetically suppress the precipitation process of Cr2N by reducing the effective residence time of the weld zone within the critical temperature range sensitive to Cr2N precipitation.Mechanical property tests show that the tensile strength and impact toughness of the welded joints exhibit a nonmonotonic trend with increasing welding current-initially decreasing,then increasing,and finally decreasing again.Optimal strength-toughness matching was achieved at 220 A.Overall,welding current plays a critical role in regulating Cr2N precipitation behavior and microstructural gradient characteristics,thereby substantially affecting the microstructure stability and mechanical properties of high-nitrogen austenitic stainless steel welded joints.关键词
高氮钢/TIG焊/微观组织/力学性能/接骨钉/医用材料Key words
high-nitrogen steel/TIG welding/microstructure/mechanical properties/bone nail/medical materials分类
矿业与冶金引用本文复制引用
王朝阳,殷子强,段鹏,姚鑫,展琰,任远,成巍..TIG焊接电流对生物医用高氮奥氏体不锈钢接头组织与力学性能的影响[J].山东科学,2026,39(2):98-107,10.基金项目
国家自然基金(51305245) （51305245）
山东省自然科学基金(ZR2020ME150) （ZR2020ME150）
山东省科技型中小企业创新能力提升工程项目(2024TSG0130,2024TSG0111,2022TSGC1130) （2024TSG0130,2024TSG0111,2022TSGC1130）