电源技术2026，Vol.50Issue(8)：1441-1445,5.DOI:10.3969/j.issn.1002-087X.2026.08.006
磷酸锰铁锂掺混三元复配电池配方研究
Research on cathode formula of composite batteries of LMFP mixed with NCM
徐艳 1林双 1徐加民 1吴涛 1蔡霞1
作者信息
- 1. 淄博火炬能源有限责任公司,山东 淄博 255056
- 折叠
摘要
Abstract
The LMFP and NCM were mixed and used as the cathode active material,and the orthogo-nal experiment method was adopted to conduct the research on the cathode formula of the compound battery.Nine cathodes formulations of the orthogonal table were processed,it was found that due to the large specific surface area of LMFP,the homogenization process required an increased stirring in-tensity and longer stirring time.Moreover,the higher the content of LMFP,the lower the solid con-tent of the slurry,and the lower the maximum compaction density of the electrode sheet.60 cycle tests were conducted on nine types of soft-pack batteries.The results show that when the LMFP∶NCM in the cathode formula is 2∶8,the PVDF addition amount is 2.5％,and the CNT addition amount is 1％,the battery had the best cycle performance.Samples of batteries were prepared using the best cathode formulation.The results show that when the specific energy is 240 Wh/kg,the com-posite battery is not suitable for high-rate discharging above 3 C.After 500 cycles,the capacity reten-tion rate of the battery is 90.12％,the battery demonstrates excellent cycling performance.关键词
磷酸锰铁锂/三元材料/复配电池/配方/电性能Key words
LMFP/NCM/the compound battery/formula/electrical performance分类
信息技术与安全科学引用本文复制引用
徐艳,林双,徐加民,吴涛,蔡霞..磷酸锰铁锂掺混三元复配电池配方研究[J].电源技术,2026,50(8):1441-1445,5.