掺锰氢氧化镍的结构与电化学性能OA北大核心CSCD
Structure and Electrochemical Performance of Mn-substituted Nickel Hydroxide
采用化学共沉淀法制备了锰取代的氢氧化镍样品,应用XRD技术对不同锰含量样品的相结构进行了表征,并用恒电流充放电、电流脉冲弛豫法和电化学阻抗技术研究了样品的电化学行为.XRD结果显示:锰含量少于20%时,样品主要由β相组成;而当锰含量达到28.3%时,可以得到具有纯α相结构的样品.电化学研究结果表明:掺锰的氢氧化镍样品具有优良的电化学循环稳定性;锰的掺杂提高了氢氧化镍电极的析氧电位,增大了样品的质子扩散系数;具有较低锰含量的氢氧化镍样品显示了较大的…查看全部>>
The Mn-substituted Ni(OH)2 samples were prepared by a coprecipitation method, and their structure was characterized by X-ray diffraction(XRD). Their electrochemical performance was also investigated by various electrochemical techniques. The results of XRD indicated that the Ni(OH)2 samples with Mn contents less than 20%mainly consist of β-phase, and the sample with a pure α structure can be obtained when the Mn content reaches 28.3%. The results of the elec…查看全部>>
吴梅银;王建明;张鉴清;曹楚南
浙江大学化学系,杭州,310027浙江大学化学系,杭州,310027浙江大学化学系,杭州,310027中国科学院金属研究所,金属腐蚀与防护国家重点实验室,沈阳,110015
化学化工
掺锰氢氧化镍电化学性能质子扩散系数
Mn-substituted Ni(OH)2, Electrochemical performance, Diffusion coefficient of proton
《物理化学学报》 2005 (5)
稳态a-Ni(OH)2的制备；结构与电化学性能的研究
523-527,5
国家自然科学基金(59902004)资助项目
评论