食品工业科技2011，Vol.32Issue(2)：240-244,5.
马铃薯淀粉耐盐性树脂的合成工艺研究
Study on synthesis craft of potato starch salt-resisting super absorbent polymer
摘要
Abstract
Without the protection of nitrogen gas, with the materials of potato starch, acrylic acid and acrylamide,ammonium persulfate as initiator with glycerol as crosslinking agent,salt-resisting super absorbent polymers was prepared by aqueous solution polymerization method, and synthesis craft of potato starch salt-resisting super absorbent polymer was optimized. The results were as follows: when mass ratios of starch to monomer was 1:7,mole ratio AA to AM was 0.5:1, degree of neutralization was 70％, reaction temperature was 60℃, the amounts of initiator, crosslinking agent were 0.25 ％ ,0.6％ ( based on the amount of monomers), respectively, cross-linking time was 1.5h. Under this condition,absorption power in 0.9％ NaCl was 76g/g, and distilled water absorption of super absorbent polymer was 786g/g.关键词
马铃薯淀粉/高吸水性树脂/接枝共聚/优化分类
轻工纺织引用本文复制引用
党斌,杨希娟..马铃薯淀粉耐盐性树脂的合成工艺研究[J].食品工业科技,2011,32(2):240-244,5.基金项目
青海省农林科学院青年创新基金. （）