锌硼玻璃基低温共烧陶瓷的微波介电性能研究
Microwave dielectric properties of zinc borate glass-based low temperature co-fired ceramics
摘要
Abstract
Zinc borate glass/ceramic composites for low temperature co-fired ceramics (LTCC) were prepared from the mixtures of zinc borate glass, Al203 and TiO2. The effects of the mass ratio of TiO2 to Al203 on the phase evolution and dielectric properties of prepared composites were investigated. The results show that the content of ZnAl2O4, TiO2 and 4ZnO · 3B203 in the composites increases, decreases,remains essentially unchanged respectively with the decrease of the mass ratio of TiO2 to Al203. The permittivity and dielectric loss of these composites increase significantly with the increase of the mass ratio of TiO2 to Al203. A near-zero temperature coefficient of resonant frequency of the composite is obtained when the mass fraction ofTiO2 is 8％.关键词
锌硼玻璃/低温烧结/微波介电性能Key words
zinc borate glass/ low temperature sintering/ microwave dielectric properties分类
化学化工引用本文复制引用
周东祥,孙荣光,胡云香..锌硼玻璃基低温共烧陶瓷的微波介电性能研究[J].电子元件与材料,2011,30(4):1-5,5.基金项目
华中科技大学材料成形与模具技术国家重点实验室自主课题 （）