电子元件与材料2011，Vol.30Issue(4)：29-32,37,5.
电泳沉积法制备纳米CoFe2O4厚膜
Electrophoretic deposition of nano-CoFe204 thick film
摘要
Abstract
Electrophoretic deposition was utilized for preparation of nano-CoFe2O4 thick film on Pt/Al203 substrates.The influence factors of electrophoretic deposition of nano-CoFe2O4 thick film were investigated. The Zeta potential value and conductivity of CoFe2O4 suspensions were measured to reflect suspension stability. The components and micromorphology of CoFe2O4 thick film were analyzed by X-ray diffraction and field emission scanning electron microscope.The ferromagnetic properties and leakage current of CoFe2O4 thick film measured by vibrating sample magnetometer and leakage current test instrument were also studied. The results show that electrophoretic deposition of CoFe2O4 thick film is feasible and the choice of deposition conditions is very important to the formation of good CoFe204 thick film. The coercive force and specific saturation magnetic moment of CoFe2O4 thick films are 225.1 kA/m and 31.17 A · m2/kg. The leakage current density is 3.0× 10-6 A/cm2.关键词
电泳沉积/CoFe2O4厚膜/铁磁性能Key words
eletrophoretic deposition/ CoFe2O4 thick film/ ferromagnetic property分类
数理科学引用本文复制引用
周东祥,郑亚楠,简刚,龚树萍..电泳沉积法制备纳米CoFe2O4厚膜[J].电子元件与材料,2011,30(4):29-32,37,5.基金项目
国家自然科学基金资助项目(No.60871017) （No.60871017）