高长径比银纳米线的制备及工艺条件研究
Synthesis and process condition of high aspect ratio silver nanowires
摘要
Abstract
Silver nanowires (Ag NWs) with high aspect ratio were one of the key materials of full printed electronic technology. Transition of reaction solution taken at different reaction time was measured by UV-visible adsorption spectra. Obtained products were characterized with XRD and SEM. Ag NWs (with an average diameter of 40 nm and length at least 50 μm) were synthesized by one-pot hydrothermal method in the presence of cetyltrimethylammonium bromide (CTAB) which acted as structure template. The morphologies of Ag nanostructures were changed by adjusting concentration of CTAB and pH value of reaction solution. High aspect ratio (≈1 300) Ag NWs are obtained when the concentration of CTAB is fixed at 5.8×10–3 mol/L and the pH of solution is 11.关键词
银/纳米线/高长径比/模板剂/一步合成/水热法Key words
silver/nanowires/high aspect ratio/template agent/one-pot synthesis/hydrothermal method分类
化学化工引用本文复制引用
成丽娟,王守绪,何为,刘慧民,彭永强..高长径比银纳米线的制备及工艺条件研究[J].电子元件与材料,2015,(2):27-30,4.基金项目
珠海市重点实验室科技攻关项目 （）