混凝土结构中钢筋锈蚀物体积膨胀率研究OA北大核心CSCDCSTPCD
Research on volumetric expansion ratio of corrosion products in concrete structure
采用通电加速锈蚀法对氯盐环境下钢筋混凝土结构保护层锈胀开裂时钢筋铁锈的体积膨胀率进行了研究．结果表明：采用低电流密度进行通电锈蚀时，钢筋铁锈的主要成分为Fe2 O3，Fe3 O4和 FeO （O H ），与自然锈蚀情况相似；通过推导分析得到了铁锈体积膨胀率的理论计算公式及其变化范围，表明铁锈的体积膨胀率仅与其所含各锈蚀产物的密度、膨胀率和质量分数有关．利用所建立公式对本研究及不同学者的试验数据进一步分析表明：混凝土中钢筋锈蚀后，生成铁锈的体积膨胀…查看全部>>
Study on volumetric expansion ratio of corrosion products at the stage of corrosive cracking of concrete cover was conducted with the method of electrifying accelerated corrosion under chloride environment .The results show that the main components of steel rusts are Fe2 O3 ,Fe3 O4 and FeO (OH) in low electric corrosion current density ,which is similar to the results in the natural corrosion condition .A theoretical formula and its variation range for calcu…查看全部>>
徐港;鲍浩;王青;徐丽丽
三峡大学土木与建筑学院，湖北宜昌443002 三峡地区地质灾害与生态环境湖北省协同创新中心，湖北宜昌443002三峡大学土木与建筑学院，湖北宜昌443002三峡大学土木与建筑学院，湖北宜昌443002
建筑与水利
钢筋混凝土通电锈蚀铁锈成分体积膨胀率理论解
reinforced concreteelectrifying corrosionrustscomponentvolumetric expansion rati-otheoretical solution
《华中科技大学学报（自然科学版）》 2015 (9)
寒区氯盐环境下在役混凝土构件受力性态衰变机理研究
105-109,5
国家自然科学基金资助项目（51109121，51379111）．
评论