电子元件与材料Issue(1)：68-72,5.DOI:10.14106/j.cnki.1001-2028.2016.01.017
氮掺杂碳包覆凹凸棒石的制备及其电化学性能研究
Preparation and electrochemical performance of attapulgite coated with nitrogen-doped carbon from polyaniline
刘信东 1应宗荣 1卢建建 1任振波 1万慧1
作者信息
- 1. 南京理工大学 化工学院 高分子材料与工程系，江苏 南京 210094
- 折叠
摘要
Abstract
The attapulgite coated with nitrogen-doped carbon was prepared by high temperature heat treatment of the attapulgite coated with polyaniline, which was synthesized by in-situ chemical polymerization of aniline. The morphology and chemical structure of the samples were characterized by scanning electron microscopy (SEM), X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR), conversion analysis for differential thermal analysis (DTA). The electrochemical performances of the composites as the electrode materials for supercapacitors were investigated by cyclic voltammetry, gslvsnostantic changing-discharging and electrochemical impedance spectroscopy. The results show that the attapulgite coated with nitrogen-doped carbon from polyaniline has a good capacitance performance in 6 mol·L–1 aqueous KOH solution, its specific capacitance can reach 161.9 F·g–1 at the scan rate of 20 mV·s–1 and it also exhibits a low inter resisitance and a good stability of the temperature coefficient of capacitance.关键词
超级电容器/碳材料/氮掺杂/包覆/凹凸棒石/电化学性能Key words
supercapacitor/carbon/nitrogen-doping/coating/attapulgite/electrochemical performance分类
信息技术与安全科学引用本文复制引用
刘信东,应宗荣,卢建建,任振波,万慧..氮掺杂碳包覆凹凸棒石的制备及其电化学性能研究[J].电子元件与材料,2016,(1):68-72,5.