Fabrication of Coupling Structure and Composite Properties by Electro-brush Plating and Laser Processing

中文摘要英文摘要

通过电刷镀‐激光加工法在铝合金表面制备出特殊的复合结构,获得具有低黏附、耐腐蚀特性的超疏水表面,其对水的静态接触角达到155.1°,滚动角小于5.6°。利用扫描电子显微镜(SEM )、光学显微镜、接触角测量仪(OCA15 Pro )和X射线衍射仪(X RD )表征表面的形貌结构、润湿特性和物相组成,并通过腐蚀性实验对表面的耐腐蚀性能进行研究。结果表明:制备表面是一种带有孔洞的沟槽与菜花状的凸包簇形成的复合结构,并且各凹槽与凸包结构均为定尺寸分布。…查看全部>>

To obtain a superhydrophobic aluminum alloy surface ,a kind of special coupling structure was fabricated on the aluminum alloy surface by a couple ways which was electro‐brush plating com‐bined with laser processing .The surface has excellent anti‐adhesion and corrosion resistance property . The contact angle can reach as high as 155 .1° ,while the sliding angle less than 5 .6° .The morphologi‐cal feature ,chemical structures ,and wettability of resultant su…查看全部>>

李晶;赵言辉;于化东;王妍;王永华;杜锋

长春理工大学机电工程学院,长春130022长春理工大学机电工程学院,长春130022长春理工大学机电工程学院,长春130022长春理工大学机电工程学院,长春130022长春理工大学机电工程学院,长春130022装甲兵技术学院机械工程系,长春130117

矿业与冶金

电刷镀激光加工超疏水低黏附耐腐蚀

electro-brush platinglaser processingsuperhydrophobiclow adhesioncorrosion resist-ance

《材料工程》 2016 (12)

微机械制造-脉冲沉积复合构建仿生疏水耦合结构及演化机制研究

28-34,7

国家自然科学基金资助项目(51505039);吉林省科技发展计划资助项目(20150204018GX );吉林省教育厅科学技术研究资助项目(22215096);中国博士后科学基金面上资助项目(2014M551145);长春理工大学青年科学基金资助项目(2021000522)

10.11868/j.issn.1001-4381.2016.12.005

评论

您当前未登录!去登录点击加载更多...