浇铸法制备的聚乳酸膜的机械特性及阻隔性能
Mechanical Characteristics and Barrier Properties of Polylactic Acid Films Prepared by Casting Method
摘要
Abstract
The tensile and barrier properties of polylactic acid (PLA) films with different polyethylene glycol (PEG) content (0wt％～20wt％) were investigated,and the effect of crystallization and aging process on these properties of the films were also evaluated.PLA films containing different PEG content were stored in conditions of 25 ℃ and 50％ relative humidity for different times.Then,the tensile properties,water vapor permeability (WVP),and oxygen permeability (OP) of the films were measured,and the microstructure of each film was examined by scanning electron microscopy (SEM).The results showed that PLA was a polymer that crystallized partially and relatively slowly.PEG could effectively plasticize PLA and promote the aging and crystallization of PLA.PEG crystals were uniformly distributed in the PLA matrix and were spherical in shape.Under the combined effect of plasticization and promotion of crystallization,the PLA film with 10wt％ PEG had a relatively high strength (tensile stress and elasticity modulus were 37.8 MPa and 1721.4 MPa,respectively) and the maximum elongation at break (63.75％).With the optimal amount of added PEG (10wt％),the minimum OP and WVP were obtained.The OP and WVP values were decreased by the simple crystallization behaviors of PLA and PEG and were increased by phase separation.In conclusion,PLA film containing 10 wt％ PEG had satisfactory tensile properties and low OP and WVP,exhibited a certain effect on blocking ultraviolet (UV) rays,and was suitable for food packaging.关键词
浇铸法/聚乳酸膜/老化/机械特性/阻隔性能Key words
casting method/polylactic acid film/aging/mechanical properties/barrier properties引用本文复制引用
朱俊友,唐传核,尹寿伟..浇铸法制备的聚乳酸膜的机械特性及阻隔性能[J].现代食品科技,2017,33(6):207-213,7.基金项目
国家自然科学基金面上项目(31471628) （31471628）
广州市珠江科技新星专项(201506010063) （201506010063）